Building retrofitting plays a key-role in energy saving and a growing interest is focused on insulating materials that allow a reduction in heat loss from envelopes with low thickness, by a process of reducing heating and cooling demand. In this context, a complete characterization of the physical properties of Moroccan natural gypsum materials was carried out. Basic information on the mineralogical, microstructure, thermal, mechanical, and acoustic characteristics of the rocks sampled from two Moroccan regions is provided. It was found that mineralogy, porosity, and water content are the main factors governing the development of the structure and the strength of the samples. The measured values of the porosity were 8.94%, the water content varied between 2.5-3.0% for the two studied typologies, coming from Agadir and Safi, respectively. Gypsum powder was used for fabricating samples, which were investigated in terms of thermal and acoustic performance. Thermal properties were measured by means of a hot disk apparatus and values of conductivity of 0.18W/mK and 0.13W/mK were obtained for Agadir and Safi Gypsum, respectively. The acoustic performance was evaluated in terms of absorption coeffcient and sound insulation, measured by means of a Kundt's Tube (ISO 10534-2). The absorption coeffcients were slightly higher than the ones of conventional plasters with similar thickness. A good sound insulation performance was confirmed, especially for Safi Gypsum, with a transmission loss-value up to about 50 dB at high frequency.
Characterization of natural gypsum materials and their composites for building applications
Merli F.Writing – Original Draft Preparation
;Buratti C.
Writing – Review & Editing
2019
Abstract
Building retrofitting plays a key-role in energy saving and a growing interest is focused on insulating materials that allow a reduction in heat loss from envelopes with low thickness, by a process of reducing heating and cooling demand. In this context, a complete characterization of the physical properties of Moroccan natural gypsum materials was carried out. Basic information on the mineralogical, microstructure, thermal, mechanical, and acoustic characteristics of the rocks sampled from two Moroccan regions is provided. It was found that mineralogy, porosity, and water content are the main factors governing the development of the structure and the strength of the samples. The measured values of the porosity were 8.94%, the water content varied between 2.5-3.0% for the two studied typologies, coming from Agadir and Safi, respectively. Gypsum powder was used for fabricating samples, which were investigated in terms of thermal and acoustic performance. Thermal properties were measured by means of a hot disk apparatus and values of conductivity of 0.18W/mK and 0.13W/mK were obtained for Agadir and Safi Gypsum, respectively. The acoustic performance was evaluated in terms of absorption coeffcient and sound insulation, measured by means of a Kundt's Tube (ISO 10534-2). The absorption coeffcients were slightly higher than the ones of conventional plasters with similar thickness. A good sound insulation performance was confirmed, especially for Safi Gypsum, with a transmission loss-value up to about 50 dB at high frequency.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.