Dual role of VEGF in pretreated experimental ePTFE arterial grafts

BACKGROUND: Lack of endothelialization and abnormal smooth muscle cell (SMC) growth adversely affect the outcome of vascular synthetic grafts. The aims of our study were to investigate how a coating of extracellular matrix (ECM) and vascular endothelial growth factor (VEGF) might affect the endothelialization rate, smooth muscle cells (SMC) proliferation, and myointimal hyperplasia in experimental arterial ePTFE grafts. METHODS: In each of 30 male Lewis rats, a 1-cm-long ePTFE graft was inserted at the level of the abdominal aorta. Animals were randomized in five groups (six animals each): groups A and A1 received ePTFE grafts coated with a synthetic extracellular matrix (growth factor-reduced matrigel) containing VEGF; groups B and B1 received ePTFE grafts coated with synthetic ECM; and group C received ePTFE grafts alone. The grafts were explanted at 30 days from surgery for immunohistochemical analysis. RESULTS: Both endothelialization rate and myointimal hyperplasia were augmented in group A versus groups B and C, and these findings were statistically significant. SMC density resulted significantly higher in group A versus groups B and C, and this was associated with an altered expression of bFGF and TGFbeta. CONCLUSIONS: Pretreating ePTFE grafts with synthetic ECM and VEGF results in better endothelialization, but also in undesired higher SMC density and myointimal hyperplasia.