We show that magnetic skyrmions can be stabilised at room temperature in continuous [Ir/Co/Pt](5) multilayers on SiO2/Si substrates without the prior application of electric current or magnetic field. While decreasing the Co thickness, a transition of the magnetic domain patterns from worm-like state to separated stripes is observed. The skyrmions are clearly imaged in both states using magnetic force microscopy. The density of skyrmions can be significantly enhanced after applying the "in-plane field procedure". Our results provide means to manipulate magnetic skyrmion density, further allowing for the optimised engineering of skyrmion-based devices.
Manipulation of Magnetic Skyrmion Density in Continuous Ir/Co/Pt Multilayers
Carlotti, G;
2022
Abstract
We show that magnetic skyrmions can be stabilised at room temperature in continuous [Ir/Co/Pt](5) multilayers on SiO2/Si substrates without the prior application of electric current or magnetic field. While decreasing the Co thickness, a transition of the magnetic domain patterns from worm-like state to separated stripes is observed. The skyrmions are clearly imaged in both states using magnetic force microscopy. The density of skyrmions can be significantly enhanced after applying the "in-plane field procedure". Our results provide means to manipulate magnetic skyrmion density, further allowing for the optimised engineering of skyrmion-based devices.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.