Despite major efforts in recent years, lignin as an abundant biopolymer is still underutilized in material applications. The production of lignin nanoparticles with improved properties through a high specific surface area enables easier applicability and higher value applications. Current precipitation processes often show poor yields, as a portion of the lignin stays in solution. In the present work, lignin was extracted from wheat straw, spruce, and beech using ethanol organosolv pretreatment at temperatures from 160-220 degrees C. The resulting extracts were standardized to the lowest lignin content and precipitated by solvent-shifting to produce lignin micro- and nanoparticles with mean hydrodynamic diameters from 67.8 to 1156.4 nm. Extracts, particles and supernatant were analyzed on molecular weight, revealing that large lignin molecules are precipitated while small lignin molecules stay in solution. The particles were purified by dialysis and characterized on their color and antioxidant activity, reaching ASC equivalents between 19.1 and 50.4 mg/mg. This work gives detailed insight into the precipitation process with respect to different raw materials and pretreatment severities, enabling better understanding and optimization of lignin nanoparticle precipitation.
Production and Properties of Lignin Nanoparticles from Ethanol Organosolv Liquors-Influence of Origin and Pretreatment Conditions
Zikeli F;
2021
Abstract
Despite major efforts in recent years, lignin as an abundant biopolymer is still underutilized in material applications. The production of lignin nanoparticles with improved properties through a high specific surface area enables easier applicability and higher value applications. Current precipitation processes often show poor yields, as a portion of the lignin stays in solution. In the present work, lignin was extracted from wheat straw, spruce, and beech using ethanol organosolv pretreatment at temperatures from 160-220 degrees C. The resulting extracts were standardized to the lowest lignin content and precipitated by solvent-shifting to produce lignin micro- and nanoparticles with mean hydrodynamic diameters from 67.8 to 1156.4 nm. Extracts, particles and supernatant were analyzed on molecular weight, revealing that large lignin molecules are precipitated while small lignin molecules stay in solution. The particles were purified by dialysis and characterized on their color and antioxidant activity, reaching ASC equivalents between 19.1 and 50.4 mg/mg. This work gives detailed insight into the precipitation process with respect to different raw materials and pretreatment severities, enabling better understanding and optimization of lignin nanoparticle precipitation.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.