This paper deals with the development of polymeric materials derived from epoxidized vegetable oils which have been used in the manufacture of laminated composite materials with basalt fabrics. Epoxidized linseed oil (ELO) and epoxidized soybean oil (ESBO) were used as biobased matrices. The basalt fabrics were modified with amino-silane and glycidyl-silane to increase fiber-matrix interactions. The curing behavior of both resins was evaluated by differential scanning calorimetry (DSC) and oscillatory rheometry (OR). The evaluation of mechanical properties was made by tensile, flexural and Charpy tests. The extent of the fiber-matrix interactions among interface was evaluated by scanning electron microscopy (SEM). The obtained results revealed that surface modification of basalt fibers with glycidyl-silane clearly improves the mechanical properties of the composites. The use of the ELO resin as matrix for composite laminates improved substantially the mechanical performance compared to composites made with ESBO.

Properties of composite laminates based on basalt fibers with epoxidized vegetable oils

Petrucci, R.;Kenny, J. M.
2015

Abstract

This paper deals with the development of polymeric materials derived from epoxidized vegetable oils which have been used in the manufacture of laminated composite materials with basalt fabrics. Epoxidized linseed oil (ELO) and epoxidized soybean oil (ESBO) were used as biobased matrices. The basalt fabrics were modified with amino-silane and glycidyl-silane to increase fiber-matrix interactions. The curing behavior of both resins was evaluated by differential scanning calorimetry (DSC) and oscillatory rheometry (OR). The evaluation of mechanical properties was made by tensile, flexural and Charpy tests. The extent of the fiber-matrix interactions among interface was evaluated by scanning electron microscopy (SEM). The obtained results revealed that surface modification of basalt fibers with glycidyl-silane clearly improves the mechanical properties of the composites. The use of the ELO resin as matrix for composite laminates improved substantially the mechanical performance compared to composites made with ESBO.
2015
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11391/1594976
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 44
  • ???jsp.display-item.citation.isi??? 36
social impact